二次冷却室利用战略定位的水喷雾喷嘴或雾化系统，对部分凝固的合金铸坯施加受控冷却。冷却强度根据实时温度监测和铸造参数精确调节，以在整个冷却室长度内保持最佳凝固速率和热分布。这确保了均匀凝固并减少缺陷。
| 参数 | 典型区间 | 选型说明与越界后果 |
|---|---|---|
| 冷却室长度 | 3000–12000 mm | Determines residence time for solidification |
| 铸坯宽度 | 200–2600 mm | Matches casting machine width |
| 铸坯厚度 | 50–400 mm | Affects cooling rate and product range |
| 拉坯速度 | 0.5–8 m/min | Higher speeds require more intensive cooling |
| 冷却水流量 | 50–500 m³/h | Per strand; varies with product size |
| 冷却水压力 | 0.3–1.0 MPa | Ensures proper spray atomization |
| 喷嘴密度 | 10–50 pcs/m² | Affects cooling uniformity |
| 冷却水温度 | 20–40 °C | Higher temperatures reduce cooling efficiency |
| 温度控制精度 | ±5 °C | Critical for metallurgical properties |
| 铸坯表面温度 | 800–1100 °C | Must be maintained within range to avoid cracks |
| 材料牌号 | 304L | Stainless steel for corrosion resistanceASTM A240 |
| 密封等级 | IP54–IP65 | Protects against water and dust ingressIEC 60529 |
| 重量 | 5–20 t | Depends on size and material |
区间为行业参考值，供询价时圈定范围用，不构成供应商承诺。下单前请向法人制造商核实每一项数值与标准。
诱因 → 失效模式 → 工程缓解
| pressure: | 0.5-3.0 bar (冷却水系统压力) |
| flow rate: | 50-500 m³/h (冷却剂流量能力) |
| temperature: | 50-300°C (冷却剂温度范围) |
不是客户评论，也不是实时热度。以下维度用于前期 RFQ 准备和供应商评估。
这些分值是采购评估维度示例，不代表真实客户评分、具体国家买家反馈或实时询盘。
它在初次凝固后对部分凝固的合金铸坯提供受控冷却，管理凝固前沿和热梯度，以确保适当的冶金组织并减少缺陷。
冷却室长度范围为3000至12000毫米，铸坯宽度为200至2600毫米，铸坯厚度为50至400毫米。这些是参考范围，必须针对具体应用进行确认。
通过水喷雾喷嘴或雾化系统控制冷却，每流流量为50-500立方米/小时，压力为0.3-1.0兆帕。温度控制精度为±5摄氏度。
冷却室采用316L不锈钢、高温陶瓷衬里和耐腐蚀喷雾喷嘴。不锈钢材料等级为ASTM A240标准下的304L。请与制造商核实。